Product Description and Application 產品描述和用途
EHLZ is a kind of flame-retardant jacketing compounds with linear low density polyethylene resin as the basic raw materials. It is mainly used as the jacketings of communication cables and control cables which have environmental-cracking resistant and flame-retardant requirements. The highest working temperature is 70℃.
EHLZ是以線性低密度聚乙烯為基材的電纜用阻燃級護層材料。主要用于耐環境開裂和阻燃要求的通信電纜、控制電纜的護層. 最高工作溫度70℃。
 
Processing Indicator 加工工藝
Recommend to use single ordinary screw extruder with L/D=20-25.
采用普通單螺桿，長徑比L/D=20-25。

Model 牌號	Machine Barrel Temperature 機筒溫度	Molding Temprature 機頭溫度
EHLZ	150-170℃	170-190℃

 
 
Physical and Electrical Properties 物理及電性能指標

Item 試驗項目	Unit 單位	Technical requirements 技術要求
Density 密度	g/cm3	≤1.0
Melt Index 熔融指數	g/10min	≤2.0
Tensile Strength 拉伸強度	MPa	≥13.0
Elongation at Break 斷裂伸長率	%	≥450
Brittle Temperature with Low Temperature 低溫脆化溫度	℃	≤-76
Resistance to Environmental Stress Cracking F0耐環境應力開裂F0	h	≥500
20℃Volume Resistivity 20℃體積電阻率	Ω·m	≥1.0×1012
20℃Dielectric Strength,50Hz 20℃介電強度, 50Hz	MV/m	≥25.0
20℃Dielectric Constant,50Hz 20℃介電常數, 50Hz	---	≤2.80
Oxygen Index 氧指數	%	≥25
200 ℃Oxidation Induction Time 200℃氧化誘導期	min	≥30